ELIFLON P-C30-000
PRECOMPOUND COPOLIMERO

INTRODUCTION

ELIFLON P-C30-000 IS A MEDIUM-LOW VISCOSITY CURE INCORPORATED COPOLYMER OF HEXAFLUOROPROPENE AND VINYLIDENE FLUORIDE. THIS GRADE OFFERS SIGNIFICANT PROCESSING EASE AND IT IS DESIGNED FOR INJECTION AND TRANSFER MOULDING.

P-C30-000 PROVIDES

  • GOOD MOULD FLOW
  • LOW MOULD FOULING
  • EASY MOULD RELEASE
  • VERY LOW COMPRESSION SET
  • VERY HIGH ELONGATION

APPLICATION

  • MOULDED GOODS, E.G. SHAFT SEALS
  • CALENDERED GOODS
  • O-RINGS, GASKETS, SEALS AND PROFILES
  • EXTRUDED CORDS
 

USE AND PROCESSING PROCEDURES

ELIFLON P-C30-000 CAN BE COMPOUNDED WITH INTERNAL MIXERS OR TWO-ROLL MILLS USING TYPICAL FLUOROELASTOMERS FILLERS AND THE OTHER INGREDIENTS.

 

SAFETY AND HANDLING

DESPITE THE CHEMICAL INERTNESS AT AMBIENT TEMPERATURE, ELIFLON P-C30-000 SHOULD BE HANDLED IN SUCH A WAY TO AVOID CONTACT WITH SKIN AND EYES. IN CASE OF CONTACT, WASH THOROUGHLY WITH SOAP AND WATER. STORE IN A WELL-VENTILATED PLACE AWAY FROM ANY SOURCE OF HEAT. SMOKING IS STRICTLY FORBIDDEN IN WORKING AND STORAGE AREAS. IN THE EVENT OF FIRE, TOXIC GASES ARE PRODUCED. REFER TO MSDS FOR ADDITIONAL INFORMATION.

FOR THE SAFE HANDLING OF OTHER COMPOUND INGREDIENTS NORMALLY USED IN FLUOROELASTOMERS COMPOUNDING, PLEASE REFER TO THE RESPECTIVE MANUFACTURERS.

{TAB DESCRIPTION}

PRODUCT DESCRIPTION

CHEMICAL COMPOSITION
 
FLUORINE CONTENT
DENSITY
COLOR
ODOR
SOLUBILITY
STORAGE STABILITY1
PHYSICAL FORM
MOONEY VISCOSITY
COPOLYMER OF HEXAFLUOROPROPENE, AND VINYLIDENE FLUORIDE PLUS CURE CHEMICALS
66%
1,81 ± 0,03 G CM-3
OFF-WHITE
NONE
ETHERS AND KETONES
EXCELLENT
SLABS
30 ± 5 {ML 1+10 @121°C}
1)AT AMBIENT TEMPERATURE IN A WELL-VENTILATED PLACE
 
CHEMICAL COMPOSITION
COPOLYMER OF HEXAFLUOROPROPENE, AND VINYLIDENE FLUORIDE PLUS CURE CHEMICALS
FLUORINE CONTENT
66%
DENSITY
1,81 ± 0,03 G CM-3
COLOR
OFF-WHITE
ODOR
NONE
SOLUBILITY
ETHERS AND KETONES
STORAGE STABILITY1EXCELLENT
PHYSICAL FORM
SLABS
MOONEY VISCOSITY
30 ± 5 {ML 1+10 @121°C}
1)AT AMBIENT TEMPERATURE IN A WELL-VENTILATED PLACE
{TAB PERFORMANCE}

PERFORMANCE OF ELIFLON P-C30-000 IN TYPICAL COMPOUND

TEST COMPOUND

 
P-C30-000
HIGH ACTIVITY MAGNESIUM OXIDE (MGO)
CALCIUM HYDROXIDE (CA(OH)2)
MEDIUM THERMAL CARBON BLACK (N990)
PROCESSING AIDS (WAX)
PHR
PHR
PHR
PHR
PHR
100
3
6
30
1
 

STOCK PROPERTIES

ODR @ 170°C, 0,5° ARC, 6 MIN.
 
ML
TS1
TS2
TC90
MH
UNIT
DNM
M.M
M.M
M.M
DNM
TYPICAL VALUE
1,03
2,36
2,84
4,90
18,24
TEST METHOD
 
 
ASTM D 6601
 
 
 

VULCANIZATE PROPERTIES

PRESS CURE 10 MIN @ 180°C, 110 KPA, POST CURE 3+15 HRS @ 230°C
 
100% MODULUS
TENSILE STRENGTH
ELONGATION AT BREAK
HARDNESS
COMPRESSION-SET 22 HRS @ 200°C
UNIT
MPA
MPA
%
SHA POINTS
%
TYPICAL VALUE
4,1
13
270
73
7
TEST METHOD
 
ASTM D 412
 
ASTM D 2240
ASTM D 395-B
 

TEST COMPOUND

 
P-C30-000
HIGH ACTIVITY MAGNESIUM OXIDE (MGO)
CALCIUM HYDROXIDE (CA(OH)2)
MEDIUM THERMAL CARBON BLACK (N990)
PROCESSING AIDS (WAX)
PHR
PHR

PHR
PHR

PHR
100
3

6
30

1
 

STOCK PROPERTIES

ODR @ 170°C, 0,5° ARC, 6 MIN.


ML
TS1
TS2
TC90
MH
UNIT

DNM
M.M
M.M
M.M
DNM
TYPICAL VALUE
1,03
2,36
2,84
4,90
18,24
TEST METHOD
 
 
ASTM D 6601
 
 
 

VULCANIZATE PROPERTIES

PRESS CURE 10 MIN @ 180°C, 110 KPA, POST CURE 3+15 HRS @ 230°C


100% MODULUS
TENSILE STRENGTH

ELONGATION AT BREAK
HARDNESS

COMPRESSION-SET 22 HRS @ 200°C
UNIT

MPA
MPA

%
SHA POINTS

%
TYPICAL VALUE
4,1
13

270
73

7
TEST METHOD
 
ASTM D 412
 
ASTM D 2240
ASTM D 395-B
 
{/TABS}
DO YOU NEED TECHNICAL OR COMMERCIAL SUPPORT?
WRITE US HERE.

Logo Sersar

© 2019 Sersar s.r.l.

Registered Office: Via Vittoria, 1 - 40068 San Lazzaro di Savena (BO) - Italy
Administrative and Operational Headquarters: Via Vittoria, 1 - 40068 San Lazzaro di Savena (BO) - Italy

Telephone: + 39.051.625.5442 | E-mail: info@sersar.net | Fax: + 39.051.625.5442
N.REA BO - 482936 - VAT N. 02987671209 | CAP.SOC. € 250.000 I.V.