ELIFLON T50-M00
TERPOLIMERO

Introduction

Eliflon T50-M00 fluoroelastomer is a medium-high viscosity terpolymer of hexafluoropropene, tetrafluoroethylene and vinylidene fluoride particularly suitable for injection moulding of sealing devices that must meet the most critical conditions of usage. Due to narrow molecular weight distribution and a low long chain branching content, despite a relative high Mooney viscosity, Eliflon T50-M00 fluoroelastomer offers significant processing ease that can be modified when blended with similar fluoroelastomers. Eliflon T50-M00 is especially suited to curing with bisphenol-phosphonium salt systems.

Provides

  • improved injection rate
  • fast curing rates
  • low mould fouling
  • easy mould release
  • good mould flow
  • improved extrusion
  • good compression set resistance

Application

  • Injection Moulded goods
  • O rings
  • Gaskets, seals and profiles
  • Extruded cords

Safety and Handling

Despite the chemical inertness at ambient temperature, Eliflon T types fluoroelastomers should be handled in such a way to avoid contact with skin and eyes. In case of contact, wash thoroughly with soap and water. Store in a well ventilated place away from any source of heat. Smoking is strictly forbidden in working and storage areas. In the event of fire, toxic gases are produced. Refer to MSDS for additional information. For the safe handling of other compound ingredients normally used in fluoroelastomers compounding, please refer to the respective manufacturers.

Description

Product Description

Chemical Composition
 
Physical Form
Color
Odor
Specific Gravity
Fluorine content
Glass transition temperature (Tg)
Solubility
Storage Stability
Mooney Viscosity, ML 1+10 at 121 °C (250 °F)
Terpolymer of hexafluoropropene, tetrafluoroethylene and vinylidene fluoride
Slabs
Off white
Odorless
1,88 ± 0,02 g/cm3
68.5 %
- 13± 1°C
Low molecular weight esters and ketones
Excellent
60 MU
Chemical Composition
Terpolymer of hexafluoropropene, tetrafluoroethylene and vinylidene fluoride
Physical Form
Slabs
Color
Off white
Odor
Odorless
Specific Gravity
1,88 ± 0,02 g/cm3
Fluorine content
68.5 %
Glass transition temperature (Tg)
- 13± 1°C
Solubility
Low molecular weight esters and ketones
Storage Stability
Excellent
Mooney Viscosity, ML 1+10 at 121 °C (250 °F)
60 MU