SEFLOR® C150-M00
COPOLIMERO

Introduction

Seflor® C150 fluoroelastomer is a high viscosity copolymer of hexafluoropropene and vinylidene fluoride particularly suitable for injection moulding of sealing devices that must meet the most critical conditions of usage.
Seflor® C150 has been specially designed to improve mechanical properties especially at elevated temperatures. Moreover, in the appropriate formulation of the compound solves the problems related to a rapid decompression.
Seflor® C150 fluoroelastomer offers significant processing ease that can be modified when blended with similar fluoroelastomers. Seflor® C150 is especially suited to curing with bisphenol-phosphonium salt systems.

Application

  • Injection Moulded goods
  • O rings
  • Gaskets, seals and profiles
  • Extruded cords

Safety and Handling

Despite the chemical inertness at ambient temperature, Seflor® C types fluoroelastomers should be handled in such a way to avoid contact with skin and eyes. In case of contact, wash thoroughly with soap and water. Store in a well ventilated place away from any source of heat. Smoking is strictly forbidden in working and storage areas. In the event of fire, toxic gases are produced. Refer to MSDS for additional information. For the safe handling of other compound ingredients normally used in fluoroelastomers compounding, please refer to the respective manufacturers.

Description

Product Description

Chemical Composition
Physical Form
Color
Odor
Specific Gravity
Fluorine content
Glass transition temperature (Tg)
Solubility
Storage Stability
Mooney Viscosity, ML 1+10 at 121 °C (250 °F)
Copolymer of hexafluoropropene and vinylidene fluoride
Slabs
Off white
Odorless
1,81 ± 0,02 g/cm3
66 %
- 18 ± 1°C
Low molecular weight esters and ketones
Excellent
150 MU
Chemical Composition
Copolymer of hexafluoropropene and vinylidene fluoride
Physical Form
Slabs
Color
Off white
Odor
Odorless
Specific Gravity
1,81 ± 0,02 g/cm3
Fluorine content
66 %
Glass transition temperature (Tg)
- 18 ± 1°C
Solubility
Low molecular weight esters and ketones
Storage Stability
Excellent
Mooney Viscosity, ML 1+10 at 121 °C (250 °F)
150 MU